Chart showing bend over sheave testing of laid rope construction
Tension Member Technology conducted bend over sheave testing of 6x9 Twaron® 3/4 inch Aramid yarn laid rope made by Whitehill Manufacturing Corporation. Ropes were constructed with and without GORE Performance Fiber for High Performance Ropes. 
Test conditions: Load, 25% of break strength; cycle rate, 500 cycles/hour; speed, 1.1 ft/sec; D:d, 20; sheave, 15 inch.
Chart showing bend over sheave testing of braided rope construction
Tension Member Technology conducted bend over sheave testing of 12-strand 3/4 inch Vectran® LCP yarn braided rope made by Cortland Cable. Ropes were constructed with and without GORE Performance Fiber for High Performance Ropes. 
Test conditions: Load, 18.5% of break strength; cycle rate, 500 cycles/hour; speed, 1.1 ft/sec; D:d, 20; sheave, 15 inch.

Twaron is a registered trademark of Teijin Aramid B.V.
Vectran is a trademark of Kuraray Co. Ltd.


Chart showing bend over sheave cycles by temperature

Reduced Rope Operating Temperatures

GORE Performance Fiber for High Performance Ropes dramatically reduces the rope surface temperature during operation.

Tension Member Technology monitored the rope surface temperature during the bend over sheave testing.  The 12-strand 3/4 inch Vectran® LCP yarn braided ropes made by Cortland Cable were constructed with and without GORE Performance Fiber for High Performance Ropes.
Test conditions: Load, 18.5% of break strength; cycle rate, 500 cycles/hour; speed, 1.1 ft/sec; D:d, 20; sheave, 15 inch.

Vectran is a trademark of Kuraray Co. Ltd.


FOR INDUSTRIAL USE ONLY

Not for use in food, drug, cosmetic or medical device manufacturing, processing, or packaging operations.

Extended Service Life

The Charts below illustrate extended service life of ropes using GORE Performance Fiber for High Performance Ropes in braided and laid rope constructions. The addition of GORE Performance Fiber for High Performance Ropes dramatically increased cycles to failure.